Product Detailed
Related Categories:PA
Related Product Searches:Flame Retardant Pigmented PA6 ( Nylon 6 ) 30%GF,High Quality,PA6, flame retardant pa6,50F30G
Excellent Balance of
High Strength, Stiffness
and Heat Distortion Temperature
Environmental Sustainability
UL-94 : V-0 g
Related Product Searches:Flame Retardant Pigmented PA6 ( Nylon 6 ) 30%GF,High Quality,PA6, flame retardant pa6,50F30G
ORACLE TM 50F30G is a 30% glass fiber reinforced, heat stabilized, flame retardant PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature.
TEST ITEMS | TEST METHOD AND CONDITIONS | TEST RESULTS | ||
TEST METHOD | UNIT | CONTITIONS | ||
(DRY)23 | ||||
Density | ISO1183-87 | g/cm3 | 1.36 | |
Melt Volume Rate | ISO1133 | cc/10min | (275)2.16kg | 9 |
Tensile strength | ISO527 | MPa | 172 | |
Tensile strain at break | ISO527 | % | 7 | |
Flexural Strength | ISO178 | MPa | 225 | |
Flexural Modulus | ISO178 | MPa | 7,000 | |
Charpy Notched | ISO183-93 | KJ/m2 | 2.9m/s-1J | 23.5 |
Heat distortion temperature | ISO75-93 | 1.8Mpa | 21 | |
Flame resistance | UL-94 | V0 | ||
Glass fibre content | % | 30±1 | ||
Processing Guidelines | ||||
Material HandlingMax. Water content: 0.12% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficient | ||||
Typical ProfileMelt Temperature 240-260 °C (464-500 °F) Mold Temperature 60-90 °C (140-194 °F) Injection and Packing Pressure 35-125 bar (500-1500 psi) | ||||
Fill RateFast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate |
Flame Retardant Pigmented PA6 ( Nylon 6 ) 30%GF